Low Carbon Steel Welding Rod / Welding Electrode AWS E6019

1) Welding Electrode AWS E6011 2) ISO9001,CE,TUV,DB,CE 3) Dia: 2.0mm,2.5mm,3.2mm;4.0mm;5.0mm;

AWS  E6019  Welding Rod / Welding Electrode

AWS E6019;JIS D4301;DIN E4343AR7

Applications:

Welding of Heavy Duty structures such as ships, vehicles, buildings and bridges.

Characteristics:

AWS E6019  is a ilmenite type electrode designed for putting emphasis on both usability and weldability. It is suitable for butt or fillet welding in all positions for thin or thicker plates (1.6 to 20mm). In horizontal fillet welding, slag covering and bead uniformity are good. Bead Appearance is very beautiful. Its usability is vertical or overhead welding is best among ilmenite type electrodes.

Notes on Usage:

(1) Pay attention not to exceed the range of proper currents. Welding with excessive current not only lowers X-ray soundness, but also causes increase of spatter, under-cut and insufficient slag covering.

(2) Dry the electrodes at 70-100 degrees C for 30-60 minutes before use. Excessive moisture absorption lowers usability and may result in some porosities.

(3) Excessive drying before use causes less in penetration and overheating of the electrode.

Typical Chemical Composition of Weld Metal (%):

C	Mn	Si	P	S
0.10	0.46	0.10	0.014	0.008

Typical Mechanical Properties of Weld Metal:

Yield Point N/mm2 (Kgf/mm2)	Tensile Strength N/mm2 (Ksi)	Elongation (%)	Impact Value Deg C, J (Deg F, Ft-lbs)
410 (60)	460 (67)	32	-18, 80 (0, 59)

Size and Recommended CurrentRange (AC or DC +):

Diameter (mm)		2.5	3.2	4.0	5.0
Length (mm)		350	350	400	400
Ampere	Flat	55-90	85-140	130-190	180-260
	V & OH	45-75	60-120	100-160	135-210

Welding Positions:

Flat, Fillet, Vertical Up, Horizontal, Overhead

Low Carbon Steel Welding Rod / Welding Electrode AWS E6019